Synthetic Slag Powder

Details

• Gurus GG+TM Fulotic Fumic De-Oxidizer cum Slag Conditioner has been well applied in SunFlag Steel Ltd, Panchmahal Steel Ltd, Rajputana Stainless Ltd, Mangalam Alloys Ltd, Virat Alloys, Shubhlaxmi Casting & many Foundries based steel plants in Bhavnagar, Baroda, Mumbai, Nagpur , Kutch, Gandhidham, Rajkot, Ankleshwar, surat, Tarapur, Punjab, Rajasthan etc.
• The quality of a variety of billet/bloom/slab produced by the continuous casting machine with GG+TM Fulotic is far better due to almost zero transfer of Slag Rich In Alumina from ladle to tundish & the qualitative production ability (lesser Alumina Stringer/inclusions or nozzle clogging) of high grade special steel & alloys.
• Steel is greatly increased with definite improvement in ladle life! Probability of early closure of ladle, thus wasting precious steel for fear of slag teeming is also reduced zero. Same material if used in the EAF or converter tapping minimizes slag tapping to less than 50kg/tapping, thus ensuring no blocking of EBT hole or oxide slag in the ladle otherwise needing high consumption of de-oxidizers.
• Benefits used by GG+TM Fulotic of Guru Metachem Pvt.Ltd are: Improving the yield rate of liquid steel:- After using 5kg/1mt GG+ Fulotic, The recovery rate of molten steel increases 0.2% to 0.6%. Based on the theoretical calculation and customers? feedback, the yield rate of liquid Metal is improved. So energy is conserved, cost of production is reduced, profit is improved.Improving the cleanliness of liquid steel:- The main factor that affects the purity of manufactured steel lies in slag entering the tundish.
• The using of GG+TM Fulotic reduces the quantity of slag to a minimum, so the steel purity is improved and the requirement of clean steel is met.
• Avoiding the clogging of nozzle:- Slag entering the dish also attributes to the clogging of nozzle when the liquid steel is re-oxidized. The application of ladle slag detection system can reduce the happening of nozzle clogging.
• Prolong service life of tundish and improve the continuous casting rate: Slag?s entering the tundish erodes the tundish.

Specifications

• Al2O3 Content (%): 30-50,3.0
• MgO Content (%): 5-10,1
• CaO Content (%): 50-60
• C12A7 : 35%

Specifications

• Al2O3 Content (%): 60-80,
• Sio2 Content (%) : 8 - 12,
• MgO Content (%): 8-10